In situ study of electrochemical activation and surface segregation of the SOFC electrode material La0.75Sr0.25r0.5 Mn0.5O3±delta

Huber, Anne-Katrin ; Falk, Mareike ; Rohnke, Marcus ; Luerßen, Bjoern ; Gregoratti, Luca ; Amati, Matteo ; Janek, Jürgen


Originalveröffentlichung: (2012) Physical chemistry, chemical physics 14(2):751 doi:10.1039/c1cp21743g
Zum Volltext im pdf-Format: Dokument 1.pdf (2.922 KB)


Bitte beziehen Sie sich beim Zitieren dieses Dokumentes immer auf folgende
URN: urn:nbn:de:hebis:26-opus-98869
URL: http://geb.uni-giessen.de/geb/volltexte/2013/9886/

Bookmark bei Connotea Bookmark bei del.icio.us


Sammlung: Allianzlizenzen / Artikel
Universität Justus-Liebig-Universität Gießen
Institut: Institute of Physical Chemistry
Fachgebiet: Chemie
DDC-Sachgruppe: Chemie
Dokumentart: Aufsatz
Sprache: Englisch
Erstellungsjahr: 2012
Publikationsdatum: 11.07.2013
Kurzfassung auf Englisch: Mixed-conducting perovskite-type electrodes which are used as cathodes in solid oxide fuel cells (SOFCs) exhibit pronounced performance improvement after cathodic polarization. The current in situ study addresses the mechanism of this activation process which is still unknown. We chose the new perovskite-type material La0.75Sr0.25Cr0.5Mn0.5O3±d which is a potential candidate for use in symmetrical solid oxide fuel cells (SFCs). We prepared La0.75Sr0.25Cr0.5Mn0.5O3±d thin film model electrodes on YSZ (111) single crystals by pulsed laser deposition (PLD). Impedance spectroscopy (EIS) measurements show that the kinetics of these electrodes can be drastically improved by applying a cathodic potential. To understand the origin of the enhanced electrocatalytic activity the surfaces of operating LSCrM electrodes were studied in situ (at low pressure) with spatially resolving X-ray photoelectron spectroscopy (µ-ESCA, SPEM) and quasi static secondary ion mass spectrometry (ToF-SIMS) after applying different electrical potentials in the SIMS chamber. We observed that the electrode surfaces which were annealed at 600 °C are enriched significantly in strontium. Subsequent cathodic polarization decreases the strontium surface concentration while anodic polarization increases the strontium accumulation at the electrode surface. We propose a mechanism based on the reversible incorporation of a passivating SrO surface phase into the LSCrM lattice to explain the observed activation/deactivation process.